Search results for "Absolute molar mass"
showing 3 items of 3 documents
Main Chain Conformation and Anomalous Elution Behavior of Cylindrical Brushes As Revealed by GPC/MALLS, Light Scattering, and SFM
1999
High molar mass polymacromonomers based on methacryloyl end-functionalized oligo methacrylates (Mn = 2410 g/mol) adopt the conformation of wormlike cylindrical brushes. Comparison of the absolute molar mass, Mw, determined by static light scattering and the contour length, Lw, of the molecules measured by SFM in the dry state revealed the length per vinylic main chain monomer of the cylindrical structure to be less than 0.1 nm, thus being much shorter than the maximum value of 0.25 nm. In solution this shrinkage could be quantified to 0.071 nm per monomer by Holtzer analysis of the scattering curves which in addition yielded the Kuhn statistical segment length lk = 120 nm. GPC MALLS investi…
Hyperbranched Poly(ethylene glycol) Copolymers: Absolute Values of the Molar Mass, Properties in Dilute Solution, and Hydrodynamic Homology
2015
Hyperbranched poly(ethylene glycol) copolymers were synthesized by random anionic ring-opening multibranching copolymerization of ethylene oxide with glycidol as a branching agent, leading to poly(ethylene glycol) structure with glycerol branching points. Extending the available range of molar masses by novel synthesis strategies, a limited extent of control over the degree of polymerization was achieved by variation of the solvent in this copolymerization. Generally, absolute molar mass characterization of hyperbranched polymers still represents an unresolved challenge. A series of the hyperbranched poly(ethylene glycol)-co-(glycerol) copolymers (hbPEGs) of a wide range of molar masses (14…
Apparent Molar Mass of a Polyelectrolyte in an Organic Solvent in the Low Ionic Strength Limit As Revealed by Light Scattering
2013
The apparent molar mass of a partially quaternized poly-2-vinylpyridines (degree of quaternization 4.3% < Q < 35%) in 1-propanol is measured by light scattering at low ionic strength (10–6 M < cs < 10–3 M) as a function of polyion repeat unit concentration (7 × 10–5 monomol/L < cm,p < 4 × 10–2 monomol/L). No dialysis was applied prior to measurements. The apparent molar mass under “salt-free” conditions is smaller than the true molar mass by an order of magnitude, while approaching the true value at higher ionic strength. Concomitant data on the dependence of scattering intensity on scattering wave vector show that the dilute polyelectrolyte solutions are strongly correlated. A recent theor…